Effect of Q-P-T Process on the Microstructure and Mechanical Properties of 300M Steel

  The effect of Quenching-Partitioning-Tempering (Q-P-T) process on the microstructure and mechanical properties of 300M steel were investigated.X-ray diffraction,scanning electron microscopy and optical microscope were employed to characterize the evolution of microstructure as well as the volume fraction of retained austenite.The results showed that the samples treated by Q-P-T possess more retained austenite compared with traditional Quenching-Tempering process.After Q-P-T,the strength increased slightly,while the ductility and toughness improved markedly.Microstructure analysis indicated the difference between Q-T and Q-P-T process lies in the amount of the retained austenite as well as the size and size distribution of the martensite laths.The Q -T resulted in a little of thin film-like retained austenite in addition to wide martensite strip,while the Q-P -T resulted in large amount of thick-like austenite accompanying narrow martensite strip.Therefore,300M steel with better ductility and toughness could be obtained by Q-P-T heat treatment.

300M steel Q-P-T Martensite Retained austenite Product of strength and elongation

Ruiwen Zhao Tianqi Liu Xinqing Zhao

School of Materials Science and Engineering, Beihang University, Beijing 100191, China Beijing Institute of Aeronautical Materials, Beijing 100095, China

国际会议

the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))

太原

英文

287-293

2012-07-13(万方平台首次上网日期,不代表论文的发表时间)