Effect of Composite Master Alloy on Mechanical Properties and Electrochemical Corrosion of ZL101 Alloy

  The mechanical properties and corrosion performances of the ZL101 alloy modified by the composite master alloy were investigated.The results showed that the master alloy had not only obvious effect of grain refinement,but also a significant role in refining dendrite grain of ZL101 alloy.The grain size decreased dramatically from 150μm to 62μm when the addition of composite master alloy is up to 0.5%(mass fraction) and the temperature is 720℃ for 30 minutes,.Its tensile strength and elongation increased by 27% and 42% respectively.The grain refinement of ZL101 alloy decreased its corrosion performance.The morphology of Si changed into globular from needle modified by NaF,instead of AlTiB.

ZL101 aluminum alloy Composite master alloy Grain refinement Corrosion performance

Hong Xu Xin Zhang Jiping Ren Min Peng Shi Yang

School of Materials Science and Engineering, North University of China, Taiyuan, 030051, China China Huadian Science and Technology Institute, Beijing 100035, China

国际会议

the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))

太原

英文

407-413

2012-07-13(万方平台首次上网日期,不代表论文的发表时间)