Synthesis and Humidity Controlling Behaviors of Sepiolite/Poly (Sodium Acrylate-Acrylamide) Composite
Sepiolite/poly (sodium acrylate-acrylamide) composite was synthesized by using inverse suspending polymerization method under different dispersant content, neutralization degree and ratio of monomer with orthogonal experiments. The surface morphology, structure and humidity controlling properties of composite were observed and determined. The results show that sepiolite/ poly (sodium acrylateacrylamide) composite is in a fine particle with rough surface. During the polymerization process, acrylate and acrylamide monomer is grafted with hydroxyl on the surface of sepiolite and then intercalated successfully into the silica layers of sepiolite. The impact of three factors on the humidity controlling behavior of composites increases by the order of dispersant content, ratio of monomer and neutralization degree. The optimum preparation parameters are dispersant content of 10％, neutralization degree of 85％ and ratio of monomer 2:1.
composite sepiolite acrylate acrylamide humidity controlling
Wang Jihui Dong Fei Ren Shuping
Tianjin Key Laboratory of Composite and Functional Materials, School of Materials Science and Engineering, Tianjin University, Tianjin 300072, China
国际会议
合肥
英文
1448-1453
2011-09-23（万方平台首次上网日期，不代表论文的发表时间）