Properties of Oxide Film on the Surface of ZrHx(x=0~2)
Oxidation behaviors of ZrHx(x=0~2) in O2 at 600℃ were investigated. The influences of temperature and oxidation time on mass gain of the oxide film were studied. The phase structure and morphology of the oxide film were analyzed by X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The result indicates that the oxidation behavior of zirconium is greatly changed after absorbing hydrogen. The oxidation rate of zirconium hydride decreased with increasing of hydrogen content. The thickness of the oxide film decreases and the uniformity of oxide film declined with increasing of x value. Some holes and creaks present in the oxide films when x value is 1.8 and 2. The similar textured oxide film on the surface of ZrHx(x=0~2) is found and the main phase of the oxide films is monoclinic ZrO2 of the baddeleyite structure. A detectable amount of tetragonal ZrO2 appeal in all the samples. A protective textured oxide film can be formed on the surface of ZrHx(x=0~2), making it ingerate and thick is important to reduce hydrogen loss.
zirconium hydride isothermal oxidation mass gain oxide film
Chen Weidong Yan Shufang Zhong Xuekui
Inner Mongolia University of Technology, Huhhot, 010051 ,China
国际会议
11th IUMRS International Conference in Asia(第十一届国际材联亚洲材料大会 IUMRS-ICA 2010)
青岛
英文
609-612
2010-09-25（万方平台首次上网日期，不代表论文的发表时间）