The Investigation of The Zirconium Silicate Coatings Prepared by APS
The zirconium silicate can be deposited as functional coatings which will be used at high temperature because of its high melting point and low thermal conductivity. It can also prevent the oxygen of the environment through the coatings and react with the substrate. In this paper, plasma spraying technology was selected to prepare the coatings of zirconium silicate. The orthogonal design method was used to optimize the parameter of plasma spraying process. The content of zirconium silicate in the coatings was checked by XRD because of the decomposition of the zirconium silicate at 1711K.The bond strength and porosity of the coatings were also measured after the optimizing of the plasma spraying parameters in this paper. According the impact on the porosity, the factors of the process can be ordered as follows: spraying distance, current, primary gases and secondary gases. And the order of spraying factors according the impact on the content of zirconium silicate in the coatings was showed as follows: spraying distance, secondary gas, primary gas and current.
zirconium silicate coating atmosphere plasma spray orthogonal design oxidation resistance
Yanbo Liu Quansheng Wang Zhuang Ma Zhong Du Juan Liu
Beijing Institute of Technology, School of Material Science and Engineering, Surface EngineeringLabo Beijing Institute of Technology, School of Material Science and Engineering, Surface Engineering Lab
国际会议
11th IUMRS International Conference in Asia(第十一届国际材联亚洲材料大会 IUMRS-ICA 2010)
青岛
英文
678-685
2010-09-25（万方平台首次上网日期，不代表论文的发表时间）