The dielectric characteristics of Sr and Mg doped CCTO ceramics
Two kinds ceramics of pure CaCu3Ti4O12 (CCTO) and Sr/Mg doped (Ca0.25Cu0.75)0.5Sr0.5TiO3 + xMgO (x=0.01, 0.03, 0.05, 0.1, denoted as CCST-M-1, CCST-M-3, CCST-M-5, CCST-M-10, respectively) were prepared using the traditional solid phase reaction method. The dielectric properties were measured by HP 4194A Impedance/Gain-Phase Analyzer with the frequency range from 100 Hz to 1MHz. The temperature dependence of dielectric constant and loss tangent were measured for different frequencies. The variation relation of the critical temperature with the frequency was fitted theoretically which is in agreement with the Arrhenius law for pure CCTO. According to a variable power law to describe the paraelectric dielectric constant of ferroelectrics with diffuse phase transitions, the theoretical fitting was carried out for doped samples, and it was suggested that all doped samples exhibited the Debye-like relaxation. Among the doped and pure CCTO samples, CCST-M-1 was of the lowest dielectric loss at the whole measurement frequency, and whose Ⅰ–Ⅴ response curve was nonlinear suggesting a non-ohmic contact. The complex-impedance analysis results showed that the reduction in dielectric loss of CCST-M-1 sample can be attributed to the increase of grain boundary resistance. It is expect that these results are helpful to promote the CCTO-related materials to practical applications.
CaCu3Ti4O12 ceramics Dielectric loss Doping
Q.X.Liu X.G. Tang Y.P.Jiang F.L.Dong
School of Physics and Optoelectric Engineering, Guangdong University of Technology,Guangzhou Higher School of Physics and Optoelectric Engineering, Guangdong University of Technology, Guangzhou Higher
国际会议
11th IUMRS International Conference in Asia(第十一届国际材联亚洲材料大会 IUMRS-ICA 2010)
青岛
英文
416-421
2010-09-25（万方平台首次上网日期，不代表论文的发表时间）