Microstructure and magnetic properties of the CoPtRu-SiO2 single and CoPtRu-SiO2/Co72Pt28-SiO2 double layer nanocomposite films
In this work, the CoPtRu nanocomposite films with were fabricated on the Ru seed layer. The effects of Ru content on the microstructure and magnetic properties of the CoPtRu-SiO2 single layer nanocomposite films, and magnetic properties of the CoPtRu-SiO2/Co72Pt28-SiO2 double layer nanocomposite films were studied. Results showed that with an increase of Ru content in the CoPtRu film, the ordering degree of hcp-CoPtRu decreased, the volume of soft magnetic fcc phase increased, both the anisotropy constant and the saturation magnetization of the CoPtRu film decreased greatly. As a result, the anisotropy field of the film did not decrease notably. Therefore, the coercivity of the CoPtRu-SiO2/Co72Pt28-SiO2 double layer film was very close to that of Co72Pt28-SiO2 single layer film at both room temperature and low temperature.
CoPtRu nanocomposites film microstructure magnetic properties
Rujun Tang Wanli Zhang Yanrong Li
State key Laboratory of Electronic Thin Films and Integrated Devices, University of ElectronicScienc State key Laboratory of Electronic Thin Films and Integrated Devices, University of ElectronicScienc State key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Scien
国际会议
11th IUMRS International Conference in Asia(第十一届国际材联亚洲材料大会 IUMRS-ICA 2010)
青岛
英文
358-363
2010-09-25（万方平台首次上网日期，不代表论文的发表时间）