Structure,Phase Composition,Physical Properties of Quenched VT16 Alloy
Features of structural and phase composition, physical and mechanical properties formation of VT16 alloy during quenching from temperature range 700875℃ were determined. For the first time formation of athermal urphase during quenching of the VT16 alloy within initial (α+β))-structure was experimentally shown. According to the summarized XRD and TEM data diagram of volume fraction variation depending on quenching temperature was proposed. Minimum of yield strength in the certain quenching temperature range was confirmed to be connected with the behavior of martensitic β→α″ -transformation during tensile testing. Fine correlation between the Youngs Module and phase composition variation was shown.
VT16 alloy quenching phase composition primary α-rphase martensite athermal ω-rphase
Anatoly Illarionov Stepan Stepanov Sergey Demakov Artemiy Popov
Ural Federal University named after the first President of Russia B. N. Yeltsin,19 Mira Str.,Ekaterinburg 620002,Russia
国际会议
The 12th World Conference Titanium(第十二届世界钛会 Ti-2011)
北京
英文
705-708
2011-06-19（万方平台首次上网日期，不代表论文的发表时间）