Manufacturing Technology of Strengthened Poplar Veneers

摘要：

Three mixed liquids, Styrene, Methylmethacrylate and Vinyl acetate were used to soak poplar veneer to obtain strengthen poplar veneers. The optimal molar ratio was fixed on 1:2:1.Soaking and polymerization technology were obtained as pressure 0.4Mpa, packing time 60 minutes, polymerization temperature 80℃, polymerization time 6 hours, cobalt naphthenate 2％, zinc chloride 6％, and azobisisobutyronitrile 3％. The impact of high temperature on the conversion was significant in the chosen level, other factors on the conversion rate was not significant.

关键词： poplar veneer strengthen manufacturing technology mixed resin

作者: Zhu Xiao-dong Wang Feng-hu Cao Jun Sun Jian-ping

作者单位: Key laboratory of Bio-Based Material Science and Technology of Ministry of Education,Northeast Forestry University,Harbin,China

会议类型: 国际会议

会议名称: 2010 International Conference on Material and Manufacturing Technology(2010材料与制造技术国际会议 ICMMT2010)

会议地点: 重庆

会议语种:英文

页码: 149-153

在线出版日期: 2010-09-17（万方平台首次上网日期，不代表论文的发表时间）