Bonding Quality of Wood-FRP Interface with Ambient Curable Epoxy Adhesives

摘要：

Effects of glue spread, adhesive kind and curing agent ratio on bonding quality of wood-FRP (Fiber Reinforced Plastic) interface were investigated to choose the optimal adhesive and condition of bonding wood-FRP composites. Two different kinds of epoxy resin and one kind of curing agent were used to bond wood-wood and wood-FRP samples with three different glue spread. Shear strength of samples were measured by compression shear test. The results indicated that bonding strength of wood-FRP sample with glue spread of 300 g/mm and curing agent ratio of 40％ were the best, when using the same epoxy resin and curing agent. The shear strengths of wood-FRP samples were less than those of samples without FRP. The bonding qualities of samples with E-44 epoxy resin/T-31 curing agent system were better than those of E-51 epoxy resin/T31 curing agent system.

关键词： FRP reinforced timber bonding quality ambient cure epoxy adhesive

作者: Fangchao CHENG Yingcheng HU

作者单位: Key Laboratory of Bio-based Material Science and Technology of Ministry of Education,Northeast Forestry University,150040,Harbin,China College of Material Science and Engineering,Northeast Forestry University,150040,Harbin,China

会议类型: 国际会议

会议名称: 2010 International Conference on Material and Manufacturing Technology(2010材料与制造技术国际会议 ICMMT2010)

会议地点: 重庆

会议语种:英文

页码: 572-575

在线出版日期: 2010-09-17（万方平台首次上网日期，不代表论文的发表时间）