Sonication-induced silk hydrogels were previously prepared as an injectable bone replacement biomaterial, with a need to improve osteogenic features. Vascular endothelial growth factor (VEGF165) and bone morphogenic protein-2 (BMP-2) are key regulators of angiogenesis and osteogenesis, respectively, during bone regeneration. Therefore, the present study aimed at evaluating in situ forming silk hydrogels as a vehicle to encapsulate dual factors for rabbit maxillary sinus floor augmentation. Sonicationinduced silk hydrogels were prepared in vitro and the slow release of VEGF165 and BMP-2 from these silk gels was evaluated by ELISA. For in vivo studies for each time point (4 and 12 weeks), 24 sinus floors elevation surgeries were made bilaterally in 12 rabbits for the following four treatment groups: silk gel (group Silk gel), silk gel/VEGF165 (group VEGF), silk gel/BMP-2 (group BMP-2), silk gel/VEGF165/BMP-2 (group V + B) (n = 6 per group). Sequential florescent labeling and radiographic observations were used to record new bone formation and mineralization, along with histological and histomorphometric analysis. At week 4, VEGF165 promoted more tissue infiltration into the gel and accelerated the degradation of the gel material. At this time point, the bone area in group V + B was significantly larger than those in the other three groups. At week 12, elevated sinus floor heights of groups BMP-2 and V + B were larger than those of the Silk gel and VEGF groups, and the V + B group had the largest new bone area among all groups. In addition, a larger blood vessel area formed in the remaining gel areas in groups VEGF and V + B. In conclusion, VEGF165 and BMP-2 released from injectable and biodegradable silk gels promoted angiogenesis and new bone formation, with the two factors demonstrating an additive effect on bone regeneration. These results indicate that silk hydrogels can be used as an injectable vehicle to deliver multiple growth factors in a minimally invasive approach to regenerate irregular bony cavities.
Wenjie Zhang David L Kaplan Xinquan Jiang Xiuli Wang Shaoyi Wang Jun Zhao Lianyi Xu Chao Zhu Deliang Zeng Jake Chen Zhiyuan Zhang
Department of Prosthodontics, Ninth Peoples Hospital, Shanghai Jiao Tong University, School of Medi Department of Biomedical Engineering, School of Engineering, Tufts University, 4 Colby St, Medford, Dalian Institute of Chemical and Physics, Chinese Academy of Sciences, Dalian 116023, China Departme Department of Oral and Maxillofacial Surgery, Ninth Peoples Hospital, Shanghai JiaoTong University, Division of Oral Biology, Tufts University School of Dental Medicine, One Kneeland Street, Boston, M