The Microstructure and Texture of Fine Grain High-Strength IF Steel after Continuous Annealing

In this paper,the fine grain high-strength IF steel after cold-rolling and continuous annealing was studied.The microstructure under different holding time of fine-grain high strength IF steel was observed by the OM and the TEM technology. The influence of texture on continuous annealing time was analysed by Electron Back-Scattering Diffraction (EBSD) technology. It is proposed that the 111 recrystallization texture of fine-grain high strength IF steel is enhanced firstly, and then is weakened along with the increase of holding time, which confirms the strongest 111 texture is occurred at 120s holding time.

fine grain high-strength IF steel texture holding time EBSD

ZHANG Li-wen WANG Zhen-min ZHANG Hong-mei ,HOU Jue

School of Materials and Engineering .University of Science and Technology Liao Ning.An shan 114000,China

国际会议

2011 International Conference on Machanical Engineering,Materials and Energy(2011年机械工程、材料与能源国际会议 ICMEME 2011)

大连

英文

1419-1424

2011-10-19(万方平台首次上网日期,不代表论文的发表时间)