Improvement of Hydrophilic Properties on Electrospun Polyacrylonitrile Fabrics Surface by plasma treatment

摘要：

Electrospun polyacrylonitrile (PAN) fabrics were prepared by electrospinning with 7％w/v concentration to dissolve in dimethylformamide (DMF) and spinning time 12 h. Radio frequency inductively couple plasma (RF-ICP)at 13.56 MHz were used to improve PAN fabrics surface by O2 gas in plasma treatment that became to hydrophilic properties of PAN fabrics surface. Physical properties were determined by scanning electron microscopy (SEM) and contact angle measurement which found that characterized on PAN fabrics surface after plasma treatment with increased treated time had been damaged on these fabrics surface which measured contact angle measurement with water were range 29.3° to 74.7°. Chemical properties were analysed by fourier transform infrared spectroscopy (FTIR) that had been found peak intensities of aliphatic C-H band at 1450 and 2930 cm-1 and peak intensities of cyclic C=O bands at 1732 cm-1 and peak intensities of saturated nitriles at 2243 cm-1 and peak intensities of hydroxyl O-H band at 3600-3650 cm-1.

关键词： Electrospun Polyacrylonitrile Fabrics Plasma Treatment Hydrophilic Surface

作者: A. Thongphud P. Visal-athaphand P. upaphol B. Paosawatyanyong

作者单位: Department of Physics, Faculty of Science, King Mongkut s University of Technology Thonburi,Bangkok Department of Physics, Faculty of Science, Chulalongkorn University, Bangkok 10330, Thailand Petroleum and Petrochemical college, Chulalongkorn University, Bangkok 10330, Thailand

会议类型: 国际会议

会议名称: 2011 International Conference on Advanced Material Research(ICAMR 2011)(2011年先进材料研究国际会议)

会议地点: 重庆

会议语种:英文

页码: 103-106

在线出版日期: 2011-01-21（万方平台首次上网日期，不代表论文的发表时间）