Effect of Annealing Temperature on Deformed Microstructure of LowCarbon Martensite

摘要：

In this paper, a new type steel plate with nanolayered martensite lath structure was produced by heavy cold-rolling. After rolling, subsequent annealing has great effect on the deformed martensite morphology and grain refinement. Microstructure recrystallizing course have occurred after long time annealing at 350°C. The recrystallization activation energy is 151 kJmol-1. The ultrafine ferrite grains (average grain size about 317nm), nano-carbides precipitated uniformly were seen in the specimen annealed at 500 °C. Annealing at and above 600 °C resulted in coarse ferrite grains with spheroidized coarse carbides, causing grain growth.

关键词： Annealing temperature Deformed microstructure Low carbon martensite

作者: Jun Zhao Yongming Yang Jiuchuan Chen Quanxing Wen Litao Zhang Shouxue Zhang Zhaokun Ren Xiangnan Wu Yuwei Gao

作者单位: North China Institute of Aerospace Engineering, Langfang 065000, China College of Materials Science North China Institute of Aerospace Engineering, Langfang 065000, China College of Materials Science and Engineering, Yanshan University, Qinhuangdao, 066004, China

会议类型: 国际会议

会议名称: 2011 International Conference on Advanced Material Research(ICAMR 2011)(2011年先进材料研究国际会议)

会议地点: 重庆

会议语种:英文

页码: 143-146

在线出版日期: 2011-01-21（万方平台首次上网日期，不代表论文的发表时间）