Influence of Temperature on Phase Composition of Nitridation Products from Rutile and Fly Ash
Rutile and fly ash powders were nitridized at different temperatures for 4 h. The influence of temperature on phase composition of nitridation products from rutile and fly ash was studied. XRD, SEM and EDS analyses show that: the phase compositions of the products was quite dependent on the reaction temperature. Mullite, O-Sialon and X-Sialon were formed from 1400 ℃ to 1450 ℃. Rising temperature would get Mullite nitrided. Meanwhile, O-Sialon and X-Sialon would be nitrided and transformed into p-Sialon. At temperatures above 1550 ℃, the main phases of the products were hexagonal columnar p-Sialon and irregular TiC0.3N0.7 grains.
Ji Haipeng Chen Kai Huang Zhaohui Liu Yangai Fang Minghao
School of Materials Science and Technology, China University of Geosciences, Beijing 10083, China