Microstructure and Properties of T2 Copper Tube Produced by Severe Hot Rolling

摘要：

In this study, the microstructure evolution as well as mechanical properties of T2 copper tube during severe hot rolling has been investigated. Owing to the severe hot rolling deformation and high rolling temperature, the microstructure of T2 copper tube evolved from initial cast structure into relatively homogenous and equiaxed grains during the process, which was testified through the results of optical microscope observation. Besides, the microhardness measurements were taken, from which the results gained were in correspondence to the microstructure transformation.

作者: Ya Li Wang Ying Liu Jing Tao Wang Fu Sheng Tian

作者单位: School of Materials Science and Engineering,Nanjing University of Science and Technology,Nanjing 210 Jiangsu Xingrong Hi-tech Company Limited,Changzhou,213000,PR China

会议类型: 国际会议

会议名称: 5th International Conference on Nanomaterials by Severe Plastic Deformation(第五届剧烈塑性变形纳米材料国际会议)

会议地点: 南京

会议语种:英文

页码: 193-198

在线出版日期: 2011-03-01（万方平台首次上网日期，不代表论文的发表时间）