Characterization of AM60 Magnesium Alloy Prepared by Rapid Solidification and Plastic Consolidation Technique
Magnesium and its alloys are attractive candidates for automotive and aerospace applications due to their relatively high strength and low density. However, their low ductility determined by hep structure of material results in limitation of plastic deformation processing. In order to improve ductility as well as mechanical properties, structure refinement processes can be used. It is well known that effective refining of the material structure can be achieved by increasing the cooling rate during casting procedures, hence rapid solidification process (RSP) has been experimented for the fabrication of magnesium alloys. The present paper reports an experimental investigation on the influence of rapid solidification on the mechanical properties of AM60 magnesium alloy. In order to obtain RS material melt spinning process was applied in protective atmosphere, resulting in formation of RS ribbons. Following consolidation of the RS material is necessary to obtain bulk material with high mechanical properties, as so hot extrusion process was applied. It was noticed that application of plastic consolidation by hot extrusion is the most effective process to achieve full densification of material. For comparison purposes, the conventionally cast and hot extruded AM60 alloy was studied as well. The purpose of the present study was to investigate in detail the effect of rapid solidification and extrusion temperature on the structure and mechanical properties of the materials.
Tomasz Tokarski
AGH University of Science and Technology,Cracow,Poland
国际会议
5th International Conference on Nanomaterials by Severe Plastic Deformation(第五届剧烈塑性变形纳米材料国际会议)
南京
英文
997-1002
2011-03-01（万方平台首次上网日期，不代表论文的发表时间）