Effect of Post Annealing Treatment on Nano-Structured Low Carbon Steel Sheets Processed by Constrained Groove Pressing
There are many works on annealing process of SPDed bulk metals but there are limited works on annealing process of SPDed sheets. Therefore, in this study the annealing response after constrained groove pressing (CGP) of low carbon steel sheets has been investigated. These sheets are subjected to severe plastic deformation at room temperature by CGP method up to three passes. Nano-structured low carbon steel sheets produced by severe plastic deformation are annealed at temperature range of 100 to 600 ℃ for 20 min. The microstructural changes after deformation and annealing are studied by optical microscopy. The effects of CGP strain and annealing temperature on microstructure, strength and hardness evolutions of the nano-scale grained low carbon steel are examined. The results show that annealing phenomena can effectively improve the elongation of process sheets with preserving the hardness and mechanical strength. Also, a thermal stability of microstructure can be observed with annealing at a temperature range of 375—425 ℃ and 400 ℃ is achieved as an optimum annealing temperature. Microstructure after post-annealing at temperatures of higher than 600 ℃ shows abnormal grain growth.
Farzad Khodabakhshi Mohsen Kazeminezhad Mohammad Azarnush Seyyed Hossein Miran
Department of Materials Science and Engineering,Sharif University of Technology,Azadi Ave.,Tehran,Iran
国际会议
5th International Conference on Nanomaterials by Severe Plastic Deformation(第五届剧烈塑性变形纳米材料国际会议)
南京
英文
1009-1014
2011-03-01（万方平台首次上网日期，不代表论文的发表时间）