Evolution of microstructure and mechanical properties of titanium Grade 4 with the Increase of the ECAP-Conform passes
This work reports on the results of investigation of microstructure change of commercially pure titanium Grade 4 with the increase of the number of ECAP-Conform passes. There has been investigated influence of continuous equal-channel angular pressing by the scheme Conform (ECAP-C) on the structure and properties of commercially pure titanium Grade 4. It has been demonstrated that as a result of first two ECAP-C cycles titanium structure is strongly fragmented and deformation bands are formed. With the further increase of ECAP-C passes to 6 the band structure is transformed into ultrafinegrained (UFG) structure with the grain size of about 250 nm. The strength of titanium regularly grows with the increase of the number of ECAP-C passes, while ductility, which settles after first cycle on the level of 12%, is almost not changed with the further strain degree increase. As a result of the subsequent drawing of titanium after ECAP-C its strength additionally increases to 1300 MPa, with retention of ductility about 11%.
Alexander V.Polyakov Dmitriy V.Gunderov Georgy I.Raab
Institute of Physics of Advanced Materials,Ufa State Aviation Technical University K.Marx St.,12,Ufa 450000,Russia
国际会议
5th International Conference on Nanomaterials by Severe Plastic Deformation(第五届剧烈塑性变形纳米材料国际会议)
南京
英文
1165-1170
2011-03-01（万方平台首次上网日期，不代表论文的发表时间）