The effect of Y on aging response and mechanical properties of Mg-Ho-Zr alloys
Mg-10Ho-0.6Zr alloys with different amount of Y additions are prepared by metal mould casting method. The effects of Y content on microstructure, age hardening behavior and mechanical properties are investigated. Results show that all the as-cast Mg-10Ho-xY-0.6Zr alloys are mainly comprised of α-Mg matrix and Mg24(Ho,Y)5 phase. With increasing Y content, grain size of the as-cast alloys is reduced. Age hardening response, Vickers hardness and mechanical properties are improved with the addition of Y. The maximum ultimate tensile strength (UTS) and yield strength (YS) are obtained in Mg-10Ho-3Y-0.6Zr alloy at peak-aged state, and the values are 215 MPa, 158 MPa at room temperature, and 144 MPa, 126 MPa at 250 ℃, respectively. The improvement of the UTS is mainly attributed to the fine distributed quadrate-like β stable phase.
Baozhong Liu Jiaojiao Liu Jianli Wang Baoqing Zhang Zhi Zhang
School of Material Science and Engineering, Henan Polytechnic University, Jiaozuo 454000,China School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710032,China
国际会议
桂林
英文
1-6
2010-11-16（万方平台首次上网日期，不代表论文的发表时间）