Comparative Analysis on the Microstructure and Property of Ni-Based Coatings Remelted by Laser and Flame
Ni60 coatings have been prepared by flame spraying and flame remelting process and by flame spraying and laser remelting process on the surface of low-carbon steel (Q235) respectively. The developed Ni60 coatings were characterized by using scanning electronic microscope (SEM), X-ray diffraction (XRD), energy dispersive spectroscopy (EDS) and micro-hardness tester. Corrosion resistance of the coatings was measured using corrosion weight loss method. The results show that the microstructure of laser remelted coatings contains fine grains and a large number of dendrites. However, the microstructure of flame remelted coatings contains coarse massive grains. In both flame remelted and laser remelted coatings the white-bright dendrites consist of γ-Ni solid solution, and grey matrix between dendrites consist of the eutectic of γ-Ni and Cr7C3, CrB, Ni3B. In addition, grey matrix between dendrites for flame remelted coatings contains the oxide phases, such as Cr2O3, NiCr2O4, Fe2O3. The even hardness of flame remelted coatings is higher than that of laser remelted coatings, but its hardness distribution is non-uniform. And corrosion resistance in sulfuric acid solution of laser remelted Ni60 coatings is superior to that of flame remelted coatings.
YUAN Qinglong FENG Xudong JI Guoliang
School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo, Henan, 454000, China
国际会议
桂林
英文
1-7
2010-11-16（万方平台首次上网日期，不代表论文的发表时间）