Study on Surface Quality of Al/SiCp Composites with Ultrasonic Vibration High Speed Milling
Al/SiCp composites with excellent physical and mechanical properties are applied widely in the aerospace, automotive, national defense, electronics and other fields. High content and high hardness SiC particles lead to poor machinability and that further application is restricted. Surface microstructure and surface formation mechanism of Al/SiCp composites were studied under condition of ultrasonic vibration milling and conventional milling. The experimental results show that machined surface had the same defects, but SiC particles were mainly direct sheared in ultrasonic milling different from the conventional milling, the roughness (Ra) of the surface generated in the ultrasonic vibration milling was smaller. At last, the formation mechanism of surface topography in the ultrasonic milling was analyzed. The research indicated that ultrasonic milling could obtain better surface quality than conventional milling and with high efficient.
Daohui Xiang Xintao Zhi Guangxi Yue Guofu Gao Bo Zhao
School of Mechanical and Power Engineering, Henan Polytechnic University, Jiaozuo 454000, China
国际会议
河南焦作
英文
1-4
2010-10-31（万方平台首次上网日期，不代表论文的发表时间）