A new type of inorganic polymer flocculant, polysilicate boron ferric and zinc sulfate (PSBFZ), was prepared through reaction of sodium silicate, ferric sulfate, zinc sulfate and sodium tetraborate. The Optimal synthesis process and material mixture ratio were determined by Orthogonal and single-factor experiments. Experimental results demonstrated that the optimal preparation conditions were as follows: the concentration of Na2SiO3 was 0.5mol/L ; polymerization time was 120 min; activation pH value was 2.2; aging time was 48h; n(B)/n(Si), n(Fe)/n(Si), n(Zn)/n(Si) were 0.4, 1.5, 1.5, respectively. PSBFZ had a favorable stability that it will not gel within 4 months. In addition, PSBFZ , an more excellent flocculant than PAC or PFS, exhibited a better flocculation performance that 93.4% of chromaticity and 97.2% of turbidity could be removed from printing and dying wastewater.
Liu zhuan-nian Cai Qian-qian Han Xiao-gang Tian Hua
College of Geology And Environment,Xi’ an University of Science and Technology Shanxi Xi’an 710054
国际会议
成都
英文
1-4
2010-06-18（万方平台首次上网日期，不代表论文的发表时间）