Synthesis and performance research of biodegradable modified polyaspartic acid
Modified polyaspartic acid (PASP-SEA-ASP) was prepared from polysuccinimide (PSI) that was thermal condensation polymer of aspartic acid (ASP), taurine (SEA) and ASP. The property of scale inhibition, dispersant and biodegradation of PASP-SEA-ASP were studied. The structure of modified polyaspartic acid was characterized by means of FTIR. Calcium carbonate crystals in scale samples were analysed by means of SEM. The results showed that under Ca2+400 mg/L, HCO3 -800 mg/L and PASP-SEA-ASP composite 4 mg/L, the scale inhibition rate of PASP-SEA-ASP was 67%. Under PASPSEA-ASP composite 15 mg/L, the least diaphaneity of the top liquid on dispersing iron oxide was 53.8 %. And PASP-SEA-ASP possess better biodegradation performance and the highest biodegradation rate can reach 70%. Modified polyaspartic acid could distort calcium carbonate crystallite and made calcium carbonate crystallite more dispersive.
Yuhua Gao Zhenfa Liu Lihui Zhang Yanji Wang
Institute of Energy Resources, Hebei Academy of Sciences Shijiazhuang, China School of Chemical Engineering and Technology Hebei University of Technology Tianjin, China
国际会议
成都
英文
1-4
2010-06-18（万方平台首次上网日期，不代表论文的发表时间）