Preparation of Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) Fiber by Dry Spinning: Drawing and Annealing

摘要：

Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) was one kind of biodegradable polyesters which were produced by a large variety of bacterium. In this work, PHBV fiber was prepared by dry spinning, followed by drawing and annealing process. The mechanical and thermal properties were determined. Tensile strength increased and the melting point decreased monotonically with draw ratio, whereas the elongation at break increased first, and then decreased. Strength of the annealed fiber increased with increasing annealing tension, while the melting point decreased slightly. The strength and elongation at break of the fibers drawn 5 times and annealed at 120 with the tension of ℃ 0.7cN/dtex could reach up to 4.7cN/dtex and 30% respectively.

作者: ZHU Shuqi YU Hao CHEN Yanmo ZHU Meifang

作者单位: College of Material Science & Engineering, Donghua University ，Shanghai 201620,P.R.China State Ke College of Material Science & Engineering, Donghua University ，Shanghai 201620,P.R.China State Key Lab.For Modification of Chemical Fibers & Polymer Materials,Donghua University, Shanghai

会议类型: 国际会议

会议名称: 2009 International Conference on Advanced Fibers and Polymer Materials(2009年先进纤维与聚合物材料国际学术会议)

会议地点: 上海

会议语种:英文

页码: 927-929

在线出版日期: 2009-10-21（万方平台首次上网日期，不代表论文的发表时间）