Effect of Severe Plastic Deformation on Microstructures and Properties of AgCuO Composites

摘要：

The microstructures and properties of AgCuO composites were researched after severe plastic deformation. The results showed that CuO particles secondly were dispersed along with increasing of true strain. The purpose of microstructure homogenization was achieved. The value of density. tensile strength and resistivity was increasing along. The value of hardness was reduced. The value of the elongation was increasing before true strain 8.0 and decreasing after true strain 8.0 in AgCuO composites.

关键词： severe plastic deformation AgCuO composites

作者: Zhou Xiaolong Cao Jianchun Li Jingtao Chen Jingchao Peng Yuanyuan Zhang Kunhua Jie Yu Feng Hao Zhang Dan

作者单位: Faculty of Materials and Metallurgy Engineering and Key Laboratory of Rare-Precious and Nonferrous M Faculty of Communication Engineering and Automatization,Kunming University of Science and Technology Kunming Institute of Precious Metal,Kunming 650221,China

会议类型: 国际会议

会议名称: Frist Annual Meeting on Testing and Evaluation of Inorganic Materials(第一届全国无机材料测试与评价学术年会)

会议地点: 南昌

会议语种:英文

页码: 49-53

在线出版日期: 2010-04-28（万方平台首次上网日期，不代表论文的发表时间）