XPS Studies on Light-Yellow Glass Prepared by Sol-Gel Dip-Coating

Light-yellow glass was prepared by coating silver film on the flat glass substrate surface with sol-gel dip-coatmg process. The chemical composition and the valence state of elements on the surface of silver thin film deposited on glass substrate were studied by X-ray photoelectron spectroscopy. Results show that: elements of Na,Mg,Ca exist in the form of their respective stable state,such as Na2O,MgO, CaO,when heat treated at 500℃ for 0.5h; but Si is unstable,and exhibit stoichiometrical disturbances. Results of chemical composition and their content by weight percent of silver thin film surface reveal that minute of quantity silver on the glass surface can lead to the glass with light-yellow color. The transmission of light for the Iight-yellow glass, deep-yellow glass and the flat glass substrate was also analyzed by spectrophotometer,and the results indicate that the light-yellow glass is capable of absorbing UV rays heavily.

Sol-gel light-yellow glass silver thin film dip-coating

Xingang Yu Kangyan Zeng Shisong Luo Hongwen Ma Wenyue Bi Huifeng Zhao Yanna Gao

College of Materials Science and Engineering,Chongqing University,Chongqing,400044,China Department of Material Science,China University of Geosciences Beijing,100083,China Research Institute of Glass and Glass Fiber,China Building Materials Academy Beijing,100024,China

国际会议

Frist Annual Meeting on Testing and Evaluation of Inorganic Materials(第一届全国无机材料测试与评价学术年会)

南昌

英文

430-432

2010-04-28(万方平台首次上网日期,不代表论文的发表时间)