Fractured Profiles Analysis of Silicone Rubber of Different Stretch Rate

摘要：

After taking five different stretch rate at the same specifications silicone rubber, and getting 10mm sample with a fracture from the teared fracture respectively, low magnification microscopy and scanning electron microscopy are used to observe the sample. Experiment results show that, with the stretch velocities increase, the tear strength of the five samples get larger. Fracture analysis shows that the tear strength is determined by stretch velocities and the uneven of the materials.

关键词： silicone rubber stretch rate fracture morphology fracture mechanism Tear strength

作者: Li Zhao Weifang Zhang Meili Ding Weiguo Hou Shengwang Liu

作者单位: School of Reliability and System Engineering, Beijing University of Aeronautics and Astronautics, Beijing, China

会议类型: 国际会议

会议名称: 2011 9th International Conference on Reliability,Maintainability and Safety(第九届国际可靠性、维修性、安全性会议 ICRMS2011)

会议地点: 贵阳

会议语种:英文

页码: 1273-1276

在线出版日期: 2011-06-12（万方平台首次上网日期，不代表论文的发表时间）