Preparation and Analyses of Nnaoclay/Nylon-6 Electrospun Nanofibers
Nylon-6 and nanoclay/nylon-6 composite nanofibers were prepared by electrospinning technique, in which formic acid was used as a solvent for good solubility of nylon-6. The diameter of nylon-6 and Nanoclay/nylon-6 were below 350 nm and had smooth surfaces. The mechanical properties of the Nanoclay/nylon-6 composite nanofibers were higher than neat nylon-6 electrospun nanofibers, which was decreased as increased the quantity of the clay. It might be due the aggregation of nanoclay at high concentration. The thermal properties of the composite nanofibers were higher than neat nylon-6 nanofibers. The DSC heating curves of nylon-6 and composites nanofibers show two endotherm behaviors, Tml (about 214 ℃) and Tm2 (about 220 ℃), corresponding to the melting events of γ-form and α-form crystals, respectively.
Nylon-6 Composite Nanofibers Electrospinning
Khalid Saeed
Department of chemistry, University of Malakand, Chakdara, Dir (Lower),N.W.F.P,Pakistan
国际会议
The 2nd International Conference on Nanomechanics & Nanocomposites(第二届国际纳米力学与纳米复合材料会议)
北京
英文
193-196
2010-10-10（万方平台首次上网日期，不代表论文的发表时间）