Study of Wheat Straw Veneer on Weave Process Bing
The wheat straw was pretreated using heat-treatment and water action and then diversified flat weave experiments were performed. Effects of the technology of knitting (including machinery spinning method, sewing spelling method, weaving process of picks one pressures one and picks two pressures two) on veneer material quality and technology of decorative facing was investigated. The results show that both of sewing spelling method and weaving process of pick two pressure two achieve better effect with close construction, level, nice appearance and simple to weave. Experiments for optimizing the technology were performed by using non-woven fabric as the laminated veneer materials, The optimal technical parameters when using non-woven fabric were as follows: MDI 1.5％and UF 8％with the dosage of 5080g/m2;temperature of 85-105℃;pressure of 0.2-0.5 MPa;time of 25min(10 sheet at a time).
Wheat straw Weave process Veneer material Non-woven fabric
Liu Fenghu Wang Anying Jiao Jianping Sun Xiaodong Zhu
Material Science and Engineering College, Northeast Forestry University, Harbin 150040 China Forestry School, Northeast Forestry University, Harbin 150040 China
国际会议
2010 International Conference on Advanced Mechanical Engineering(2010年先进机械工程国际学术会议 AME 2010)
洛阳
英文
1027-1031
2010-09-04（万方平台首次上网日期，不代表论文的发表时间）