Design of experiments for determination of influence of different parameters on mechanical properties of semi-solid extruded parts
Near net-shape production of complex parts with higher mechanical properties is one of the most important final goals of the recent researches on the semi-solid processing. Having the knowledge of the influence of every parameter on the properties of final parts is the key in the production of high quality complex parts. Among these parameters forming temperature and velocity, and reheating and holding times have the greatest effects on the final mechanical properties of the parts. The influence of the parameters of non-dendritic billet production, forming speed, temperature and holding time on the properties of semi-solid extruded parts were investigated. Cooling-slope method was employed in order to produce non-dendritic billets. The material used was A356 aluminum alloy. Since the number of the parameters influencing the final properties of the parts was high (these parameters include: cooling slope angle, ram velocity, temperature and holding time), the final number of the experiments required would be n4, in which n is the number of the states of the parameters (5 in our case). In order to reduce this amount, design of experiments Tachuchi method was employed (design L25). Using this method the number of required experiments was reduced to 25. For the experiments the prepared semisolid samples were extruded under isothermal condition and with 5 different ram speeds. Standard tensile tests were conducted on the extruded parts and the mechanical properties of the parts were determined. The obtained results analyzed with MiniTab and the influence of each of the parameters and also the percentage of its influence were calculated. Finally an optimum region for the parameters was determined. The temperature, ram speed, slope angle and holding time have more important effects descendingly.
semi-solid extrusion Tachuchi method A356 alloy mechanical properties
V.POUVAFAR S. A. SADOUGH F. HOSSEINJ M. R. RAHMANI
Center of Excellence in Solid Mechanics, Mechanical Engineering Department,AmirKabir University of Technology (Tehran Polytechnic), 15914 Tehran, Iran
国际会议
北京
英文
794-797
2010-09-16（万方平台首次上网日期，不代表论文的发表时间）