Electro-pulse modification and reheating process forproduction of thixotropic microstructure in AlSi7Mg alloy
Electro-pulse modification (EPM) was used to change the dendritic structure of AlSi7Mg alloy to globular one. The effects of the modified temperature, electro-pulse frequency and time on the solidified structure were examined. The results show that these parameters play an important role in the solidified microstructures. That is to say, under the same modified temperature, the solidified microstructure will be improved greatly with the increase of electro-pulse frequency and time, but when they exceed to limit values, the solidified microstructure will become worse, resulting from the decrease of the ratio of nucleation. The experimental results indicate that the suitable modified temperature of AlSi7Mg alloy is 720 ℃, and the appropriate electropulse frequency and time are 5 Hz and 40 s, respectively. Then the microstructures produced by suitable EPM process were reheated at temperatures between liquidus and solidus, the primary-Al grains ripen further and become more spherical, which is favorable to the semi-solid forming of AlSi7Mg alloy.
AlSi7Mg alloy semi-solid alloy electro-pulse modification reheating process
TIAN Wen-tong ZHANG Guang-an
College of Mechanical and Electrical Engineering, Changzhou Institute of Technology, Changzhou 21300 College of Material and Chemical Engineering, Liaoning Industrial University, Jinzhou 121001, China
国际会议
北京
英文
943-947
2010-09-16（万方平台首次上网日期，不代表论文的发表时间）