The Effect of Random Spectrum on the Fatigue Life of Hybrid Metal Matrix Composites
This research makes comparisons of empirical fatigue-lives between AC8A Al alloy and the metal matrix composites (Al/Al2O3, Al/Al2O3/Al2O3P), and also includes comparisons of fatigue-lives between empirical fatigue-lives and estimated fatigue-lives from regular-periodic load testing, acoustic emission (AE) method to predict fatigue-crack initiation before visible in sight and SEM (Scanning Electron Microscope) photographs of each material. According to the test results of the notched specimen, the fatigue life of the hybrid metal matrix composites and the metal matrix composites, which are more brittle than the base matrix was shorter than that of the base matrix under both types of loads. In addition, the fatigue-life estimated from the damage summation method and that from experiments at random loads were fairly identical.
Random spectrum Fatigue life Acoustic emission Hybrid Metal Matrix Composites
Yi Qi Wang Hyung Kun Ku Gi Beop Nam Jung Il Song
Dept. of Mechanical Engineering, Changwon National University, Korea
国际会议
沈阳
英文
336-341
2010-07-28（万方平台首次上网日期，不代表论文的发表时间）