Study on the feasibility of bacterial cellulose as tissue engineering scaffold
OBJECTIVE: As a kind of nanometer natural material, bacterial cellulose (BC) has been widely used in the field of food processing, paper making, pharmaceutical science, etc. In recent years, it is found that there is a good application potentiality of BC used in the medical science, especially in the field of regeneration medicine. There are some reports about BC being used in tissue engineering. It is of great necessity to investigate its tissue compatibility. In this research, the cell compatibility of BC was studied by using the method of cell-culturing combined with rat adipose- derived stem cells (ADSCs) as the seed cells. MATERIAL and METHODS: BC membranes were prepared by Key Laboratory of Industrial Microbiology, Ministry of Education, Tianjin University of Science and Technology. The average pore size and porosity of it were 0.8-3.5μm and 93％, respectively. The ADSCs were isolated from the fat pad located in pars inguinalis of 3-weeks Wistar rats by using type II collagenase and then cultured using DMED medium contained 10％ new-born calf serum. The status of cell growth was observed everyday. The cell growth curve was determined by MTT method and stem cell phenotype was identified by flow cytometry. Cells in exponential phase of growth were planted on the surface of BC membrane which had been sterilized beforehand by steam at 121℃ for 20 min at cell density of 3.0×105 cells/mL. The cell-BC compound was cultured by using DMED medium contained 10％ new-born calf serum. The growth status and the biological characterization of ADSCs cultured on the BC were determined at different culture time. RESULTS: Most ADSCs primary cultured in vitro showed fusiform shape when they were cultured for 72 hours. The amount of the cells increased along with the culture time and confluenced at 7 days. The exponential phase of growth of primary cultured ADSCs in vitro appeared when they were cultured for 3 to 9 days. The result of flow cytometry showed that ADSCs could express the stem cell symbol. The portait section of cell-BC compound were made after 10 days cultured in vitro. It was shown that ADSCs compact grew on the surface of BC. CONCLUSION: It is indicated that ADSCs grew on the BC membrane still retain the biological activity of stem cell and BC has good biocompatibility. It might be further studied for BC as tissue engineering scaffold.
bacterial cellulose adipose-derived stem cells tissue engineering scaffold
Wang Ping Shi Yi Jia Yuanyuan Zheng Jingtong Wang Zongliang Chen Yanyan Zhou Yulai
Otolaryngology-Head and Neck Surgery, First Hospital, Jilin University, Changchun 130021, Jilin Prov Experimental Center of Bioengineering, School of Pharmaceutical Sciences, Jilin University, Changchu College of Material Science and Chemical Engineering, Tianjin Science and technology University, Tia Experimental Center of Bioengineering, School of Pharmaceutical Sciences, Jilin University, Changchu
国际会议
青岛
英文
147-150
2009-10-09（万方平台首次上网日期，不代表论文的发表时间）