Controlled Fabrication of Nanocomposite with Ni Deposition on the Template of SiO2 Particles and its Magnetic Property
SiO2 /Ni nanocomposite is directly prepared from the silica particle by a controllable method through electroless metallization, which is different from the sol-gel technique. Its fabrication procedure is as follows: first the formation of ligating monolayer by a silane agent coupling with silica, then, binding Pd catalyst with its ligating group, finally, nano-sized Ni deposition occurs on the template. The metallic Ni particles are uniformly deposited on the silica, and they have a net or chain-like structure, just as the silica particles do. The composite inherent coercivity (iHc), saturated magnetization (MS), and residual magnetization (Mr) are 16.5, 10.0 and 1.00 respectively in the as-plated Ni. The chain-like structure causes stronger static magnetization interactions between Ni particles, resulting in a magnetic crystalline anisotropy and the higher iHc value.
Silica powder controlled fabrication electroless deposition of Ni nanocomposite structure magnetic property
Yu-bin Fu Xue-rong Zai
Institute of Material Science and Engineering, Ocean University of China, Qingdao 266100 College of Chemistry and Chemical Engineering, Ocean University of China, Qingdao 266100
国际会议
青岛
英文
501-504
2009-10-09（万方平台首次上网日期，不代表论文的发表时间）