Preparation of WS2/MoS2/C Composite Films and their Tribological Properties

摘要：

WS2/MoS2/C composite lubricating films were prepared in an Ar/C2H2 atmosphere by magnetron reaction-sputtering using a WS2/MoS2 composite target. The relationship between the microstructure and the tribological performance of the films was investigated. The composite film has a compact microstructure, which is shown to have much superior tribological performance with lower friction coefficient and better wear resistance than pure MoS2 film in humid atmospheric conditions at room temperature. An increase in hardness of nearly one order of magnitude was reached, too.

关键词： WS2 MoS2 C Friction and Wear Properties

作者: ZHOU Lei YIN Gui-lin WANG Yu-dong YU Zhen HE Dan-nong

作者单位: College of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, China National Engineering Research Center for Nanotechnology, Shanghai 200241, China College of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, China

会议类型: 国际会议

会议名称: 第二届多功能材料与结构国际会议

会议地点: 青岛

会议语种:英文

页码: 711-714

在线出版日期: 2009-10-09（万方平台首次上网日期，不代表论文的发表时间）