Effect of Heat Treatment on Optical Properties of Cold Spray TiO2 Coated Glass

摘要：

The cold spray TiO2 thin films were deposited on 5mm-thick float glass substrates using the sol containing nano-anatase TiO2. The effects of different heat treatment temperatures on optical properties were discussed. The properties of xerogel powder were analyzed using TG-DSC, the morphology and structure of TiO2 thin films were characterized by FESEM and XRD, the transmittance and absorption of TiO2 coated glass were investigated by UV-vis spectrophotometer. The results reveal that TiO2 in the film is still anatase phase after heat treatment at 350℃ and 500℃. With the annealing temperatures increasing from 20℃ to 500℃, the average crystal size increases just from 21.4 nm to 23.9nm, UV absorption of TiO2 coated glass increases from 2.2 to 2.7, visible light transmittance is high to about 80％.

关键词： TiO2 coated glass TiO2 thin film cold spray heat treatment optical property

作者: Jingkai Yang Hongli Zhao Yanli Liu Fucheng Zhang

作者单位: College of Materials Science and Engineering, Yanshan University, Qinhuangdao Hebei, China State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao

会议类型: 国际会议

会议名称: 第二届多功能材料与结构国际会议

会议地点: 青岛

会议语种:英文

页码: 803-806

在线出版日期: 2009-10-09（万方平台首次上网日期，不代表论文的发表时间）