Adhesion and Corrosion Resistance Properties of TiC/Ti(CN)/TiN Multilayer CVD Coatings on 42CrMo Steels
The TiC/Ti(CN)/TiN multilayer coatings were deposited on 42CrMo steel by chemical vapor deposition (CVD) method. The fracture morphology,structure,microhardness and adhesion of the coatings were analyzed. The immersion test in simulant solution with H2S,CO2 at 100°C and electrochemistry test in 20wt％ H2SO4 at room temperture were applied to investigate the corrosion resistance of the multilayer films.The results reveal that the multilayer coatings can offer 42CrMo steel higher corrosion resistance,especially the immersion corrosion test.The corrosion rate of the samples coated with CVD multilayer films is reduced more 70 times than that of the uncoated and samples by quenching-polishing-quenching (QPQ) treat.
TiC/Ti(CN)/TiN multilayer coatings CVD corrosion behavior adhesion
Zhang Jin Xue Qi Cheng Xiaowei Zhang Chunmei Li Songxia
School of Materials Science & Engineering, Southwest Petroleum University Chengdu 610500 P.R.China
国际会议
青岛
英文
1009-1012
2009-10-09（万方平台首次上网日期，不代表论文的发表时间）