Microstructure evolution and mechanical properties of 7A09 aluminum alloy during rapid solidifications

Microstructure evolution and mechanical properties of 7A09 aluminum alloy ribbon prepared by rapid cooling solidification are studied. Single roller is applied to produce rapid solidification ribbon of 7A09 aluminum alloys. Microstructure characteristics and mechanical properties of the rapid solidified ribbon of 7A09 aluminum alloys are studied by means of X-ray diffraction (XRD), scan electron microscopy (SEM) and hardness measurement. The results show that the rotate speed of the roller is the key factor affecting the ability of the forming ribbon. At a roller rotate speed of 1500rpm, the ribbon with a good quality can be obtained. Microstructure features of the rapid solidification ribbon are refined with the increase of the cooling rate, all of the crystals translate into nanocrystalline. All the hardness of the rapid solidification ribbon of 7A09 aluminum alloys is higher than that of the original alloys and increases with the rotate speed of the rotor.

single roller 7A09 aluminum alloy rapid solidification

Weiwei Wang Binbin Jia Jingbo Yu

School of Materials Science and Engineering, Harbin Institute of Technology (Weihai) Weihai, P.R.China, 264209

国际会议

第二届多功能材料与结构国际会议

青岛

英文

1791-1794

2009-10-09(万方平台首次上网日期,不代表论文的发表时间)