Solid-State Synthesis and Characterization of Nanocrystalline Rare Earth Compound under Ultrasonication
Under near ambient temperature and ultrasonication, the La(Oxin)3·H2O (lanthanum 8-quinolinolate) nanocrystallite was synthesized by solid-state reaction. The solid phase was characterized by powder X-ray diffraction (XRD) and electron diffraction (ED). The particle size, its distribution, and morphology of the prepared nanocrystallite were observed by transmission electron microscopy (TEM). Results showed that the product was nanocrystallite with a uniform particle size and with an average size of about 50 nm, and the yield rate of nanocrystalline La(Oxin)3?H2O is approximately 95.9 ％. During the synthesis of La(Oxin)3·H2O nanocrystallite, the types of factors influencing the final product under different solid-state reaction conditions such as reactant, changing the proportions of reactant, addition of inert substances, mixing of trace solvent or surfactant and time of porphyrizing was also observed.
lanthanum 8-quinolinolate nanocrystallite supersonic wave solid-state synthesis characterization
Daohua Li
College of Chemistry and Life Science Neijiang Normal University Neijiang, China
国际会议
成都
英文
193-196
2009-09-25（万方平台首次上网日期，不代表论文的发表时间）