Dispersion Polymerization of Acrylamide and Acrylic Acid in Aqueous Media
Dispersion polymerization of acrylamide and acrylic acid was successfully carried out in aqueous salt solutions using anionic polyelectrolytes as stabilizers. The influences of aqueous solution of salt concentration, molecular weight and concentration of the stabilizers on the apparent viscosity and stability of the dispersions, and on the molecular weight of the polymers prepared were investigated. The results showed that stable dispersions could be obtained on condition that salt concentration was between 26％～30％, concentration of stabilizers between 8％～12％, and intrinsic viscosity of stabilizers between 2.977～3.740 dL/g. With salt concentration ranging from 26％ to 30％, molecular weight of products increased first and then decreased. Molecular weight of products was hardly changed when concentration of stabilizer was between 8％～12％. When intrinsic viscosity of stabilizer was between 2.977～3.740 dL/g, increase of the molecular weight of stabilizer resulted in a decrease in the molecular weight of the products.
Dispersion polymerization acrylamide acrylic acid aqueous media
Jiao Lu Bo Peng Mingyuan Li Meiqin Lin
Enhanced Oil Recovering Research Centre, China University of Petroleum (Beijing), China
国际会议
2009 Advanced Polymer Processing(Qingdao)Intl Forum(2009高分子材料先进制造业(青岛)国际论坛
青岛
英文
233-238
2009-08-19（万方平台首次上网日期，不代表论文的发表时间）