Study on the Microstructure and Deformation Behavior of Ultrafine-crystalline Cu-Y Ribbons

Cu99.8Y0.2, Cu99.2Y0.8 and Cu98Y2 alloy ribbons were prepared by single roller melt spinning. The microstructure was studied by X-ray diffraction (XRD), transmission electron microscopy (TEM), high voltage electron microscope (HVEM) and high resolution electron microscopy (HREM). The results showed that α-Cu was the dominative phase in the rapid solidification ribbons of three alloys. A secondary phase Cu4Y was detected in the Cu98Y2 ribbon by XRD. The grain size was in a range of 50-200 nm in the Cu99.2Y0.8 and Cu98Y2 ribbons. Many nano-scale twins and some dislocations existed inside the larger grains. However, the grains in Cu99.8Y0.2 ribbon were in the size of microns and the sub-grains with small misorentations were in 100-200 nm. To understand the deformation mechanism, in situ tensile test were carried out at a High Voltage Electron Microscope (HVEM). The results showed that the deformation is predominated by the dislocation slip in larger grains. To accommodate the deformation, elastic deformation occured in the small grains in the initial stage of the deformation. Meanwhile, some small grains maybe deform by grain rotations. With strain increasing, some fractures generated and propagated along the grain boundaries or across the grains.

Cu-Y Ribbon Microstructure Deformation Behavior TEM HVEM HREM

Z. W. DU Z. M. SUN B. L. SHAO A. S. LIU

General Research Institute for Nonferrous Metals, Beijing, 100088

国际会议

2008年中美材料国际研讨会

重庆

英文

591-597

2008-06-09(万方平台首次上网日期,不代表论文的发表时间)