Fabrication of nano-crystalline W-Ni-Fe pre-alloyed powders by mechanical alloying technique
Nano-crystalline pre-alloyed powders of W-Ni-Fe were fabricated by high energy ball milling mechanical alloying (MA) technique. The change of appearances and the crystallite sizes of powders before and after high energy ball milling were investigated by XRD, TOPAS P software, SEM and EDS. The results show that the nano-crystalline pre-alloyed powders can be fabricated by 5 h high energy ball milling. During the MA process, the diffusion of W, Ni and Fe happens in the process of repeated welding and fracturing. As a result, nano-crystalline supersaturated solid solutions are formed. The crystallite sizes wont be refined after 10 h ball milling. The crystallite sizes of different compositions are almost the same under the same MA condition. Due to the toughening mechanism of rare earth element, the powders of 90W4Ni-2Fe-3.8Mo-0.2RE alloy are seriously agglomerated after ball milling compared with the other alloys. It can be concluded that the optimal sintering temperature of 90W-4Ni-2Fe-3.8Mo-0.2RE pre-alloyed powders after 15 h mechanical alloying is 1 300-1 350 ℃.
tungsten based high-density alloy mechanical alloying high energy ball milling nano-crystalline low temperature sintering
YAN Jian-wu LIU Ying PENG A-fang LU Quan-guo
Institute of Micro/Nano Actuation and Control, Nanchang Institute of Technology, Nanchang 330099, Ch Postdoctoral Station of Nanchang University, Nanchang 330034, China Institute of Micro/Nano Actuation and Control, Nanchang Institute of Technology, Nanchang 330099, Ch
国际会议
2009 Frontier Symposium of China Postductors on Materrials Science(2009年中国博士后材料科学前言论坛)
长沙
英文
711-717
2009-11-22（万方平台首次上网日期，不代表论文的发表时间）