Residual strains of aluminum alloy characterized by nanoindentation

摘要：

A formula was brought forward to correlate residual strain with hardness measured by nanoindentation method. Using the formula, residual strains in prestrained aluminum alloy samples were evaluated. In order to compare with the calculated strain, such values were also measured by strain gauge method. The results show that the differences of the residual strain obtained by nanoindentation and strain gauge method are not more than 8%, which shows that the formula is suitable for characterizing residual strain of aluminum alloy.

关键词： aluminum alloy residual strain nanoindentation hardness strain gauge

作者: WANG Yan-shen QU Shi-liang GAI Yu-xian DONG Shen LIANG Ying-chun

作者单位: Department of Physics, Harbin Institute of Technology, Harbin 150001, China School of Naval Architec Department of Optoelectronic Science, Harbin Institute of Technology at Weihai, Weihai 264209, China School of Naval Architecture, Harbin Institute of Technology at Weihai, Weihai 264209,China Center for Precision Engineering,Harbin Institute of Technology, Harbin 150001, China

会议类型: 国际会议

会议名称: 2009 Frontier Symposium of China Postductors on Materrials Science(2009年中国博士后材料科学前言论坛)

会议地点: 长沙

会议语种:英文

页码: 767-771

在线出版日期: 2009-11-22（万方平台首次上网日期，不代表论文的发表时间）