Thermomechanical effect on magnetic behaviors of antiferromagnetic Mn-Fe(Cu) alloy

摘要：

The effect of thermomechanical treatment on the magnetic properties of Mn85.5Fe9.0Cu0.5 alloy was studied by use of a materials testing machine, a vibrating sample magnetometer, an X-ray diffractometer, a homogeneously and adjustably magnetic field and strain gauges. The results show that the orientation of fct phase and magnetic domains is affected by the thermomechanical treatment. When the compressive strain of thermomechanical treatment is-1.2%, the magneticfield-induced strain reaches the highest value in the adapted situation.

关键词： thermomechanical treatment antiferromagnetic Mn-Fe(Cu) alloy magnetic-field-induced strain magnetization curve

作者: PENG Wen-yi CAI Fen-min WANG Xiao-yu ZHANG Ji-hua YANG Xiang-jie ZHANG Ai-sheng YAN Ming-ming ZOU Hai-yang

作者单位: School of Materials Science and Engineering, Nanchang University, Nanchang 330031, China School of Materials, Arizona State University, Tempe, AZ85287, USA School of Materials Science and E School of Materials, Arizona State University,Tempe, AZ85287, USA School of Mechatronics Engineering,Nanchang University,Nanchang 330031, China School of Materials Science and Engineering, Nanchang University, Nanchang 330031,China School of Materials Science and Engineering,Nanchang University, Nanchang 330031, China

会议类型: 国际会议

会议名称: 2009 Frontier Symposium of China Postductors on Materrials Science(2009年中国博士后材料科学前言论坛)

会议地点: 长沙

会议语种:英文

页码: 802-805

在线出版日期: 2009-11-22（万方平台首次上网日期，不代表论文的发表时间）