Influence of arrangement field on magnetostrictive and mechanical properties of magnetostrictive composites

Non-aligned and aligned polymer-bonded Tb0.3Dy0.7Fe2 composites with 20% particle volume fraction were prepared under different arrangement fields (I.e.0,10 kA/m,20 kA/m,30 kA/m,60 kA/m and 100 kA/m) during their gel process.Static magnetostriction,dynamic magnetostriction,elastic modulus and compressive strength of all specimens were tested and compared.Experimental results indicate that all the parameters are positively dependent on the arrangement field.The dependence is significant at low field levels,the critical value of which is 30 kA/m for the composites fabricated.No obvious improvement of the properties can be observed for a larger field.Such critical values are defined as the optimal arrangement field to manufacture magnetostrictive composites.

magnetostrictive composites Terfenol-D arrangement field magnetostriction

DONG Xu-feng GUAN Xin-chun QI Min OU Jin-ping

School of Materials Science and Engineering,Dalian University of Technology,Dalian 116024,China School of Civil Engineering,Harbin Institute of Technology,Harbin 150090,China School of Civil Engineering,Harbin Institute of Technology,Harbin 150090,China;School of Civil and H

国际会议

2009 Frontier Symposium of China Postductors on Materrials Science(2009年中国博士后材料科学前言论坛)

长沙

英文

1454-1458

2009-11-22(万方平台首次上网日期,不代表论文的发表时间)