STUDY ON THE TI-DOPED SILICA GEL ADSORPTIVE FUNCTIONAL PAPER
The novel Ti-doped silica gel adsorptive functional paper was prepared by treating ceramic fiber paper with sequential impregnation of water glass and acidic titanyl sulfate solution. In FTIR spectra, the peak at about 954 cm-1 is the characteristic of Ti-OSi bond of the Ti-doped silica gel. SEM photograph reveals that the particles of Ti-doped silica gel are well scattered on the surface and in the apertures of the ceramic fiber paper. According to the changes of Si2p,O1s,Ti2p3/2 binding energy from XPS, as well as the difference of silica atom chemical shift from 29Si MAS NMR before and after Ti-doping, it can be inferred the substitution insertion of titanium into the silica gel framework. BET analysis shows that the novel adsorptive paper possess a high BEt specific surface areas above 410m2·g-1, in which the mesopores are majority. The Ti-doping increases the specific surface area and pore volume, leading to the improvement of adsorptive capacity and thermal stability of silica gel functional paper.
Ti-doped silica gel Ceramic fiber SEM
Liang Xianghui Fang Yutang Fu Shiyu
The State Key Laboratory of Pulp and Paper Engineering, South China University of Technology, Guangz The Key Laboratory of Enhanced Heat Transfer & Energy Conservation, Ministry of Education, South Chi The State Key Laboratory of Pulp and Paper Engineering, South China University of Technology, Guangz
国际会议
广州
英文
488-492
2006-11-08（万方平台首次上网日期，不代表论文的发表时间）