Dielectric and Electrical Studies of SrBi2Nb1.9V0.1O9 Ferroelectric Ceramics

摘要：

In the present work, effect of sintering temperature on structural, dielectric and electrical properties of vanadium substituted strontium bismuth niobate ferroelectric ceramics have been studied. Samples of composition SrBi2Nb1.9V0.1O9 were synthesized by solid-state reaction method at different sintering temperatures. X –ray diffraction analysis reveals the formation of perovskite structure. Peak dielectric constant is found to increase with increasing sintering temperature while Curie temperature is observed to be the highest in the sample sintered at 900 oC and it decreases in the sample sintered at 1000 oC. Impedance analysis of the samples was carried out to study the grain and the grain boundary effects. Cole-cole plots reveal a decrease in bulk resistance on increasing temperature indicating NTCR behavior.

关键词： Ferroelectrics Curie temperature Dielectric constant Dielectric

作者: Sameer Jain Sheela Devi A.K. Jha

会议类型: 国际会议

会议名称: 2009 The 18th IEEE International Symposium on Applications of Ferroelectrics(2009年国际铁电学暨IEEE国际铁电应用联合会议)

会议地点: 西安

会议语种:英文

页码: 95-99

在线出版日期: 2009-08-23（万方平台首次上网日期，不代表论文的发表时间）