Fabrication and Characterization of HAp/Al2O3 Composite Coating on Titanium Substrate

摘要：

HAp/Al2O3 composite coating was fabricated onto micro-arc oxidized titanium substrate using a combination of electrophoretic deposition and reaction bonding process. SEM, EDS and XRD were employed to characterize the titanium substrate and as-prepared coatings. The interfacial bonding strength of the sintered composite coating was tested by shear strength testing experiment. Results show that the green form composite coating can be easily sintered with no cracks and decomposition at 850, the bonding strength to the substrate is significantly improved compared with the single HAp coating.

关键词： Hydrozyapatite Composite coating Electrophoretic deposition Reaction bonding process

作者: Zhou-Cheng Wang Yong-Jin Ni Jin-Cong Huang

作者单位: Department of Chemical and Biological Engineering Xiamen University, Xiamen, China

会议类型: 国际会议

会议名称: The 2nd International Conference on Bioinformatics and Biomedical Engineering(iCBBE 2008)(第二届生物信息与生物医学工程国际会议)

会议地点: 上海

会议语种:英文

页码: 1526-1530

在线出版日期: 2008-05-16（万方平台首次上网日期，不代表论文的发表时间）