MICROSTRUCTURE AND MECHANICAL PROPERTIES OF HYPEREUTECTIC Al-Si/AINp COMPOSITE
Hypereutectic Al-Si alloys with fine and evenly distributed Si precipitates have superior mechanical properties In this study, hypereutectic Al-Si alloy powders which contained 15 and 20wt％ Si were prepared by a gas atomization process. 1, 3 and 5wt％ AlN particles were blended with the Al-Si alloy powders using turbular mixer. The mixture was consolidated by Hot Press at 550℃ for 1h under 60MPa. Relative density of the sintered samples was about 98％ of theoretical density. This study was investigated by two ways. One is the effect of reinforcement weight fraction and the other is the effect of Silicon contents on the mechanical properties of the composite. Microstructural characterization and phase evaluation were carried out using X-ray Diffraction, Scanning Electron Microscopy equipped with Energy Dispersive Spectrometer. The results showed that the smaller the reinforcement particle size was and the better its distribution was, the higher ultimate tensile strength and hardness were.
Hypereutectic Al-Si mechanical property AIN
SEULKI PARK JINMYUNG CHOI BONGGYU PARK IKMIN PARK YONGHO PARK YONGJIN KIM
School of Materials Science and Engineering, Pusan National University, 30 Jangjeon-dong, Geumjeong- Korea Institute of Machinery and Materials, Powder Materials Research Center, 66 Sangnam-dong, Chang
国际会议
第五届先进材料与加工国际会议(Fifth International Conference on Advanced Materials and Processing ICAMP-5)
哈尔滨
英文
1377-1382
2008-09-03（万方平台首次上网日期，不代表论文的发表时间）